Acoustic wave device, high frequency front end circuit, and communication apparatus

ABSTRACT

An acoustic wave device includes a piezoelectric substrate made of LiNbO3, and a dielectric film provided on the piezoelectric substrate to cover first and second IDT electrodes on the piezoelectric substrate. The first and second IDT electrodes include main electrode layers. When wave lengths determined by electrode finger pitches of the first and second IDT electrodes are λ1 and λ2, respectively, the average value thereof is λ0, λ1/λ0=1+X, and λ2/λ0=1−X, a relationship of 0.05≤X≤0.65 is satisfied. The wavelength λ1 is the longest, and the wavelength λ2 is the shortest. In Euler angles (φ, θ, ψ) of the piezoelectric substrate, φ is 0°±5°, ψ is 0°±10°, and θ satisfies Expression 1, wherein a relationship of B1&lt;T×r≤0.10λ0 and B2&lt;T×r≤0.10λ0 are satisfied.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of priority to Japanese Patent Application No. 2017-081432 filed on Apr. 17, 2017 and is a Continuation Application of PCT Application No. PCT/JP2018/014221 filed on Apr. 3, 2018. The entire contents of each application are hereby incorporated herein by reference.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates to an acoustic wave device using a Rayleigh wave, a high frequency front end circuit, and a communication apparatus.

2. Description of the Related Art

In recent years, there has been a growing need for increasing the speed of data communication in mobile information terminals, and therefore a technique to simultaneously perform communication in a large number of bands by carrier aggregation or the like, a technique to widen a bandwidth also in an individual band, and the like are needed. At the same time, since mobile information terminals are always required to be miniaturized, acoustic wave devices used in the mobile information terminals are also required to be even more miniaturized.

In order to meet the requirement for miniaturization, there is a demand for a technique to provide a plurality of band pass filters having different pass bands on the same piezoelectric substrate. For this purpose, it is necessary to form a plurality of interdigital transducer (IDT) electrodes having largely different electrode finger pitches on the same piezoelectric substrate. Also in a case where a single filter is formed on the same piezoelectric substrate, there is a demand for a technique to form a plurality of IDT electrodes having largely different electrode finger pitches on the same piezoelectric substrate in order to widen the bandwidth.

In International Publication No. WO 2017/006742, an example of an acoustic wave device is described. The acoustic wave device utilizes a Rayleigh wave propagating through a piezoelectric substrate made of LiNbO₃. A dielectric layer is provided on the piezoelectric substrate to cover an IDT electrode.

SUMMARY OF THE INVENTION

Preferred embodiments of the present invention provide acoustic wave devices, high frequency front end circuits, and communication apparatuses each able to effectively reduce or prevent unwanted waves even when a plurality of IDT electrodes with different electrode finger pitches is provided on the same piezoelectric substrate.

An acoustic wave device according to a preferred embodiment of the present invention includes a piezoelectric substrate made of LiNbO₃, a plurality of IDT electrodes provided on the piezoelectric substrate and including a first IDT electrode and a second IDT electrode, and a dielectric film provided on the piezoelectric substrate to cover the plurality of IDT electrodes. Further, the first IDT electrode and the second IDT electrode include main electrode layers. When a wave length determined by an electrode finger pitch of the first IDT electrode is λ₁, a wave length determined by an electrode finger pitch of the second IDT electrode is λ₂, an average value λ₀ of the wave length λ₁ and the wave length λ₂ is defined by an equation of λ₀=(λ₁+λ₂)/2, λ₁/λ₀=1+X, and λ₂/λ₀=1−X, a relationship of 0.05≤X≤0.65 is satisfied. Among the plurality of IDT electrodes, the wave length λ₁ of the first IDT electrode is the longest and the wave length λ₂ of the second IDT electrode is the shortest. When a film thickness obtained by normalizing, with the average value λ₀, at least one of film thicknesses of the main electrode layer of the first IDT electrode and the main electrode layer of the second IDT electrode is T, and a density ratio of a material of the main electrode layer to Pt is r, in Euler angles (φ, θ, ψ) of the piezoelectric substrate, φ is 0°±5°, ψ is 0°±10°, and θ satisfies Expression 1. −A ₁/(T×r−B ₁)+C ₁ ≤θ≤−A ₂/(T×r−B ₂)+C ₂  Expression 1

A relationship of B₁<T×r≤0.10λ₀ and a relationship of B₂<T×r≤0.10λ₀ are satisfied, and A₁, B₁, C₁, A₂, B₂, and C₂ in the Expression 1 are represented by Expression 2 through Expression 8 below using X. A ₁=0.056×10^(−4.93×x)+0.0016  Expression 2 B ₁=−0.088×X ²+0.066×X+0.0386(0.05≤X≤0.375)  Expression 3 B ₁=0.051(0.375≤X≤0.65)  Expression 4 C ₁=0.714×10^(−5.26×x)+28.37  Expression 5 A ₂=0.0987×X ²−0.0918×X+0.0644  Expression 6 B ₂=−0.0651×X ²+0.1114×X+0.0351  Expression 7 C ₂=0.7830×X ²−1.7424×X+32.70  Expression 8

An acoustic wave device according to a preferred embodiment of the present invention includes a piezoelectric substrate made of LiNbO₃, a plurality of IDT electrodes provided on the piezoelectric substrate and including a first IDT electrode and a second IDT electrode, and a dielectric film provided on the piezoelectric substrate to cover the plurality of IDT electrodes. Further, the first IDT electrode and the second IDT electrode include main electrode layers. When a wave length determined by an electrode finger pitch of the first IDT electrode is λ₁, a wave length determined by an electrode finger pitch of the second IDT electrode is λ₂, an average value λ₀ of the wave length λ₁ and the wave length X2 is defined by an equation of λ₀=(λ₁+λ₂/2, λ₁/λ₀=1+X, and λ₂/λ₀=1−X, a relationship of 0.05≤X≤0.65 is satisfied. Among the plurality of IDT electrodes, the wave length λ₁ of the first IDT electrode is the longest and the wave length λ₂ of the second IDT electrode is the shortest. When a film thickness obtained by normalizing, with the average value λ₀, at least one of film thicknesses of the main electrode layer of the first IDT electrode and the main electrode layer of the second IDT electrode is T, and a density ratio of a material of the main electrode layer to Pt is r, in Euler angles (φ, θ, ψ) of the piezoelectric substrate, φ is 0°±5°, ψ is 0°±10°, and θ satisfies Expression 1. −A ₁/(T×r−B ₁)+C ₁ ≤θ≤−A ₂/(T×r−B ₂)+C ₂  Expression 1

A relationship of B₁<T×r≤0.12λ₀ and a relationship of B₂<T×r≤0.12λ₀ are satisfied, and A₁, B₁, C₁, A₂, B₂, and C₂ in the Expression 1 are represented by Expression 2 through Expression 8 using X. A ₁=0.056×10^(−4.93×x)+0.0016  Expression 2 B ₁=−0.088×X ²+0.066×X+0.0386(0.05≤X≤0.375)  Expression 3 B ₁=0.051(0.375≤X≤0.65)  Expression 4 C ₁=0.714×10^(−5.26×x)+28.37  Expression 5 A ₂=0.0987×X ²−0.0918×X+0.0644  Expression 6 B ₂=−0.0651×X ²+0.1114×X+0.0351  Expression 7 C ₂=0.7830×X ²−1.7424×X+32.70  Expression 8

In an acoustic wave device according to a preferred embodiment of the present invention, a film thickness and a material of the main electrode layer of the first IDT electrode are the same or substantially the same as a film thickness and a material of the main electrode layer of the second IDT electrode, and a film thickness of a portion of the dielectric layer provided on the first IDT electrode is equal or substantially equal to a film thickness of a portion of the dielectric film provided on the second IDT electrode.

In an acoustic wave device according to a preferred embodiment of the present invention, the dielectric film includes silicon oxide as a main ingredient. In this case, it is possible to improve frequency-temperature characteristics.

In an acoustic wave device according to a preferred embodiment of the present invention, a plurality of band pass filters belonging to communication bands of different pass bands are provided on the piezoelectric substrate.

In an acoustic wave device according to a preferred embodiment of the present invention, an antenna terminal to be connected to an antenna is provided on the piezoelectric substrate, and the plurality of band pass filters are connected commonly to the antenna terminal to define a composite filter.

In an acoustic wave device according to a preferred embodiment of the present invention, a composite filter is not defined by the plurality of band pass filters.

A high frequency front end circuit according to a preferred embodiment of the present invention includes an acoustic wave device according to a preferred embodiment of the present invention, and a power amplifier.

A communication apparatus according to a preferred embodiment of the present invention includes a high frequency front end circuit according to a preferred embodiment of the present invention, and an RF signal processing circuit.

With the acoustic wave devices, the high frequency front end circuits, and the communication apparatuses according to preferred embodiments of the present invention, it is possible to effectively reduce or prevent unwanted waves even when a plurality of IDT electrodes having different electrode finger pitches is provided on the same piezoelectric substrate.

The above and other elements, features, steps, characteristics and advantages of the present invention will become more apparent from the following detailed description of the preferred embodiments with reference to the attached drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view of an acoustic wave device according to a first preferred embodiment of the present invention.

FIG. 2 is a schematic elevational cross-sectional view of the acoustic wave device according to the first preferred embodiment of the present invention.

FIG. 3 is a schematic plan view illustrating an electrode structure of a first acoustic wave resonator in the first preferred embodiment of the present invention.

FIG. 4 is an enlarged elevational cross-sectional view of a first IDT electrode in the first preferred embodiment of the present invention.

FIG. 5 is a graph showing return loss when a wave length of an IDT electrode of an acoustic wave resonator of a comparative example is set to about 1.00λ₀.

FIG. 6 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 0.90λ₀.

FIG. 7 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 0.95λ₀.

FIG. 8 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 1.05λ₀.

FIG. 9 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 1.10λ₀.

FIG. 10 is a graph showing return loss when a wave length of an IDT electrode of an acoustic wave resonator of the first preferred embodiment of the present invention is set to about 1.00λ₀.

FIG. 11 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment of the present invention is set to about 0.90λ₀.

FIG. 12 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment of the present invention is set to about 0.95λ₀.

FIG. 13 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment of the present invention is set to about 1.05λ₀.

FIG. 14 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment of the present invention is set to about 1.10λ₀.

FIG. 15 is a graph showing return loss of an acoustic wave resonator in which a wave length of an IDT electrode is about 1.00λ₀, in the case where θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate is about 28°.

FIG. 16 is a graph showing return loss of the acoustic wave resonator of the present invention in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 29°.

FIG. 17 is a graph showing return loss of the acoustic wave resonator of the present invention in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 30°.

FIG. 18 is a graph showing return loss of the acoustic wave resonator of the present invention in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 31°.

FIG. 19 is a graph showing return loss of the acoustic wave resonator of the present invention in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 32°.

FIG. 20 is a graph showing a relationship between θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate and a fractional bandwidth of an unwanted wave, in an acoustic wave resonator in which a wave length of an IDT electrode is about 1.00λ₀.

FIG. 21 is a graph showing a relationship among a wave length of an IDT electrode in an acoustic wave resonator, θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate, and a fractional bandwidth of an unwanted wave, in the case where X is about 0.05.

FIG. 22 is a graph showing a relationship between a film thickness of a main electrode layer and upper and lower limit values of θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate at which a fractional bandwidth of an unwanted wave in an acoustic wave resonator is equal to or smaller than about 0.005%, in the case where X is about 0.05.

FIG. 23 is a graph showing a relationship among a wave length of an IDT electrode in an acoustic wave resonator, θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate, and a fractional bandwidth of an unwanted wave, in the case where X is about 0.10.

FIG. 24 is a graph showing a relationship between a film thickness of a main electrode layer and upper and lower limit values of 0 in Euler angles (φ, θ, ψ) of a piezoelectric substrate at which a fractional bandwidth of an unwanted wave in an acoustic wave resonator is equal to or smaller than about 0.005%, in the case where X is about 0.10.

FIG. 25 is a graph showing a relationship among a wave length of an IDT electrode in an acoustic wave resonator, θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate, and a fractional bandwidth of an unwanted wave, in the case where X is about 0.15.

FIG. 26 is a graph showing a relationship between a film thickness of a main electrode layer and upper and lower limit values of θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate at which a fractional bandwidth of an unwanted wave in an acoustic wave resonator is equal to or smaller than about 0.005%, in the case where X is about 0.15.

FIG. 27 is a graph showing a relationship among a wave length of an IDT electrode in an acoustic wave resonator, θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate, and a fractional bandwidth of an unwanted wave, in the case where X is about 0.20.

FIG. 28 is a graph showing a relationship between a film thickness of a main electrode layer and upper and lower limit values of θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate at which a fractional bandwidth of an unwanted wave in an acoustic wave resonator is equal to or smaller than about 0.005%, in the case where X is about 0.20.

FIG. 29 is a configuration diagram of a communication apparatus including a high frequency front end circuit according to a preferred embodiment of the present invention.

FIG. 30 is a graph showing a transmission characteristic of an acoustic wave filter when spurious noise having a size of about 0.2 dB is generated within a pass band of the acoustic wave filter.

FIG. 31 is a graph showing a transmission characteristic of an acoustic wave filter when spurious noise having a size of about 0.27 dB is generated within a pass band of the acoustic wave filter.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Hereinafter, the present invention will be clarified by describing specific preferred embodiments of the present invention with reference to the accompanying drawings.

The preferred embodiments described herein are illustrative and a partial substitution or combination of configurations may be possible between different preferred embodiments.

FIG. 1 is a schematic view of an acoustic wave device according to a first preferred embodiment of the present invention.

An acoustic wave device 1 includes an antenna terminal 12 to be connected to an antenna, and a plurality of band pass filters connected commonly to the antenna terminal 12. The pass bands of the plurality of band pass filters are different from each other. The acoustic wave device 1 of the present preferred embodiment is a composite filter device used for carrier aggregation or the like.

The plurality of band pass filters includes a first band pass filter 3A, a second band pass filter 3B, and a third band pass filter 3C. The acoustic wave device 1 also may include a band pass filter other than the first band pass filter 3A, the second band pass filter 3B, and the third band pass filter 3C. The number of band pass filters is not particularly limited.

Among the plurality of band pass filters, the pass band of the first band pass filter 3A is located on the lowest frequency side. On the other hand, among the plurality of band pass filters, the pass band of the second band pass filter 3B is located on the highest frequency side.

Here, the acoustic wave device 1 includes a piezoelectric substrate. The first band pass filter 3A and the second band pass filter 3B are provided on the same piezoelectric substrate.

The first band pass filter 3A includes a plurality of acoustic wave resonators including a first acoustic wave resonator. Similarly, the second band pass filter 3B includes a plurality of acoustic wave resonators including a second acoustic wave resonator. The first band pass filter 3A, the second band pass filter 3B, and the third band pass filter 3C may preferably be ladder filters, for example, or may include a longitudinally coupled resonator acoustic wave filter. It is sufficient that the first band pass filter 3A includes at least the first acoustic wave resonator. It is sufficient that the second band pass filter 3B includes at least the second acoustic wave resonator. The circuit configurations of the first band pass filter 3A, the second band pass filter 3B, and the third band pass filter 3C are not particularly limited.

FIG. 2 is a schematic elevational cross-sectional view of the acoustic wave device according to the first preferred embodiment.

A piezoelectric substrate 2 illustrated in FIG. 2 is preferably made of LiNbO₃, for example. In the present preferred embodiment, preferably, in Euler angles (φ, θ, ψ) of the piezoelectric substrate 2, φ is 0°±5° and ψ is 0°±10°, for example. Note that, θ in the Euler angles (0°±5°, θ, 0°±10°) will be described later. In this specification, for example, 0°±5° indicates a range from −5° to 5°.

On the piezoelectric substrate 2, the first acoustic wave resonator 13A and the second acoustic wave resonator 13B are provided. In FIG. 2 , although the first acoustic wave resonator 13A and the second acoustic wave resonator 13B are disposed at positions adjacent to each other, the arrangement of the first acoustic wave resonator 13A and the second acoustic wave resonator 13B is not particularly limited.

FIG. 3 is a schematic plan view illustrating an electrode structure of the first acoustic wave resonator in the first preferred embodiment.

The first acoustic wave resonator 13A includes a first IDT electrode 4A provided on the piezoelectric substrate. When an AC voltage is applied to the first IDT electrode 4A, an acoustic wave is excited. The acoustic wave device 1 uses a Rayleigh wave as an acoustic wave. Reflectors 7 a and 7 b are disposed on both sides of the first IDT electrode 4A in an acoustic wave propagation direction.

The first IDT electrode 4A includes a first busbar 5 a and a second busbar 6 a opposing each other. The first IDT electrode 4A includes a plurality of first electrode fingers 5 b whose one ends are connected to the first busbar 5 a. Further, the first IDT electrode 4A includes a plurality of second electrode fingers 6 b whose one ends are connected to the second busbar 6 a. The plurality of first electrode fingers 5 b and the plurality of second electrode fingers 6 b are interleaved with each other.

FIG. 4 is an enlarged elevational cross-sectional view of the first IDT electrode in the first preferred embodiment.

The first IDT electrode 4A includes a main electrode layer 14 a provided on the piezoelectric substrate 2, and a conductive auxiliary electrode layer 14 b provided on the main electrode layer 14 a. In the present specification, the main electrode layer is a metal layer that occupies the largest mass among the metal layers constituting the IDT electrode.

Although the material used for the first IDT electrode 4A is not particularly limited, the main electrode layer 14 a is preferably made of, for example, Pt in the present preferred embodiment. In addition to Pt, a metal having a relatively high density, such as Au, W, Mo or Cu, may preferably be used for the main electrode layer 14 a. The conductive auxiliary electrode layer 14 b is preferably made of, for example, Al. By including the conductive auxiliary electrode layer 14 b having relatively low electric resistance, the electric resistance of the first IDT electrode 4A is able to be lowered. The reflectors of the first acoustic wave resonator are preferably made of metal layers that are the same as or similar to those of the first IDT electrode 4A.

In the present preferred embodiment, the first IDT electrode 4A includes the main electrode layer 14 a and the conductive auxiliary electrode layer 14 b, and it may include a close contact layer. The close contact layer can be disposed, for example, between the piezoelectric substrate 2 and the main electrode layer 14 a, or on the conductive auxiliary electrode layer 14 b. For the close contact layer, NiCr, Ti, or Cr may preferably be used, for example. A diffusion preventing layer may be provided between the main electrode layer 14 a and the conductive auxiliary electrode layer 14 b. For example, Ti may preferably be used for the diffusion preventing layer. Note that the first IDT electrode 4A may include only the main electrode layer 14 a.

Similarly to the first acoustic wave resonator, the second acoustic wave resonator also includes a second IDT electrode 4B illustrated in FIG. 2 , and reflectors. Other acoustic wave resonators of the first band pass filter and the second band pass filter also include, respectively, IDT electrodes and resonators. In the present preferred embodiment, the film thicknesses and materials of the first IDT electrode 4A and reflectors, the second IDT electrode 4B and reflectors, and other IDT electrodes and reflectors of the first band pass filter and the second band pass filter are preferably substantially the same. In this specification, “substantially the same” means that the film thicknesses and materials are the same to the extent that the deterioration in electric characteristics of the acoustic wave device 1 does not occur. For example, in practice, even when IDT electrodes, reflectors, and the like are provided as to have the same film thickness, a manufacture variation in film thickness is generated. However, in the case where the difference in film thickness is such that the deterioration in the electric characteristics is not caused, the film thicknesses may be considered to be substantially the same.

Here, a wave length determined by an electrode finger pitch of the first IDT electrode 4A is defined as λ₁, and a wave length determined by an electrode finger pitch of the second IDT electrode 4B is defined as λ₂. At this time, among the wave lengths of the plurality of IDT electrodes, the wave length λ₁ of the first IDT electrode is the longest, and the wave length λ₂ of the second IDT electrode is the shortest. In the present preferred embodiment, when an average value λ₀ of the wave lengths λ₁ and λ₂ is obtained by an equation of λ₀=(λ₁+λ₂/2, λ₁/λ₀=1+X, and λ₂/λ₀=1−X, a relationship of 0.05≤X≤0.65 is satisfied.

As illustrated in FIG. 2 , a first dielectric film 8 is provided on the piezoelectric substrate 2. The first dielectric film 8 covers the first IDT electrode 4A, the second IDT electrode 4B, and the reflectors. The thickness of a portion of the first dielectric film 8 provided on the first IDT electrode 4A and the thickness of a portion thereof provided on the second IDT electrode 4B are equal or substantially equal.

In the present preferred embodiment, the first dielectric film 8 preferably includes, as a main ingredient, silicon oxide such as SiO₂, for example. This makes it possible to lower the absolute value of a temperature coefficient of frequency and improve the frequency-temperature characteristics. In addition, the surfaces of the plurality of IDT electrodes are protected, and the plurality of IDT electrodes are unlikely to be damaged. In this specification, the term “main ingredient” refers to an ingredient occupying equal to or greater than about 50% by weight. The material of the first dielectric film 8 is not limited to the above, and may be, for example, silicon oxynitride, tellurium oxide, or the like.

A second dielectric film 9 is provided on the first dielectric film 8. In the present preferred embodiment, the second dielectric film 9 is preferably made of, for example, silicon nitride such as SiN. By adjusting the film thickness of the second dielectric film 9, frequency adjustment can be easily performed. The material of the second dielectric film 9 is not limited to the above, and may be, for example, aluminum oxide, aluminum nitride, or silicon oxynitride.

The present preferred embodiment includes the piezoelectric substrate 2 made of LiNbO₃, the plurality of IDT electrodes provided on the piezoelectric substrate 2 and including the first IDT electrode 4A and the second IDT electrode 4B, and the first dielectric film 8 provided on the piezoelectric substrate 2 to cover the plurality of IDT electrodes, and further has a structure as follows. (1) In the first IDT electrode 4A and the second IDT electrode 4B, λ₁/λ₀<1+X, λ₂/λ₀=1−X, and a relationship of 0.05≤X≤0.65 is satisfied. (2) When the film thickness obtained by normalizing, with the average value λ₀, at least one of the film thicknesses of the main electrode layer of the first IDT electrode 4A and the main electrode layer of the second IDT electrode 4B is T, and the density ratio of the material of the main electrode layer to Pt is r, θ in the Euler angles (0°±5°, θ, 0°±10°) of the piezoelectric substrate 2 satisfies Expression 1 through Expression 8 given below. Note that the density ratio r is a value obtained by dividing the density of the material of the main electrode layer by the density of Pt. −A ₁/(T×r−B ₁)+C ₁ ≤θ≤−A ₂/(T×r−B ₂)+C ₂  Expression 1

A relationship of B₁<T×r≤0.10λ₀ and a relationship of B₂<T×r≤0.10λ₀ are satisfied. A₁, B₁, C₁, A₂, B₂, and C₂ in the above Expression 1 are represented by Expression 2 through Expression 8 below using X. A ₁=0.056×10^(−4.93×x)+0.0016  Expression 2 B ₁=−0.088×X ²+0.066×X+0.0386(0.05≤X≤0.375)  Expression 3 B ₁=0.051(0.375≤X≤0.65)  Expression 4 C ₁=0.714×10^(−5.26×x)+28.37  Expression 5 A ₂=0.0987×X ²−0.0918×X+0.0644  Expression 6 B ₂=−0.0651×X ²+0.1114×X+0.0351  Expression 7 C ₂=0.7830×X ²−1.7424×X+32.70  Expression 8

With the above structure, it is possible to effectively reduce or prevent unwanted waves even when a plurality of IDT electrodes having different electrode finger pitches are provided on the same piezoelectric substrate. This will be described below by comparing the first preferred embodiment with a comparative example.

The comparative example is different from the first preferred embodiment in that Euler angles (φ, θ, ψ) of the piezoelectric substrate do not satisfy the Expression 1. The acoustic wave used in the first preferred embodiment and the comparative example is a Rayleigh wave, and a shear horizontal (SH) wave is an unwanted wave.

The wave length of an IDT electrode of an acoustic wave resonator of the first preferred embodiment and the wave length of an IDT electrode of an acoustic wave resonator of the comparative example were varied to compare return loss characteristics thereof. The average value λ₀ of the wave length λ₁ of the first IDT electrode and the wavelength λ₂ of the second IDT electrode was taken as a reference value, and then the wave length was varied in a range from about 0.90λ₀ to about 1.10λ₀. In the first preferred embodiment, the following conditions were used.

Piezoelectric substrate: Material LiNbO₃, Euler angles (0°, 30°, 0°)

Main electrode layer: Material Pt, Film thickness about 0.085λ₀

Conductive auxiliary electrode layer: Material Al, Film thickness about 0.08λ₀

Duty ratio: about 0.60

First dielectric film: Material SiO₂, Film thickness about 0.35λ₀

Second dielectric film: Material SiN, Film thickness about 0.01λ₀

In the comparative example, the following conditions were used.

Piezoelectric substrate: Material LiNbO₃, Euler angles (0°, 19°, 0°)

Main electrode layer: Material Pt, Film thickness about 0.0425λ₀

Conductive auxiliary electrode layer: Material Al, Film thickness about 0.08λ₀

Duty ratio: about 0.60

First dielectric film: Material SiO₂, Film thickness about 0.35λ₀

Second dielectric film: Material SiN, Film thickness about 0.01λ₀

FIG. 5 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 1.00λ₀. FIG. 6 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 0.90λ₀. FIG. 7 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 0.95λ₀. FIG. 8 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 1.05λ₀. FIG. 9 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the comparative example is set to about 1.10λ₀. In these graphs, the horizontal axis represents a normalized frequency normalized with a resonant frequency of each acoustic wave resonator.

As shown in FIG. 5 , in the comparative example, when the wave length of the IDT electrode is set to about 1.00λ₀, spurious noise is suppressed. However, as shown in FIGS. 6 to 9 , when the wavelength is equal to or smaller than about 0.95λ₀ and also when the wave length is equal to or greater than about 1.05λ₀, it is understood that a large spurious noise is generated due to the unwanted wave.

When λ is about 0.10, λ₁ is about 1.10λ₀ and λ₂ is about 0.90λ₀, and the return loss characteristics of the first acoustic wave resonator correspond to FIG. 9 and the return loss characteristics of the second acoustic wave resonator correspond to FIG. 6 . At this time, in a case where any value in the range from about 0.90λ₀ to about 1.10λ₀ is the wave length of the IDT electrode, it is preferable to reduce or prevent spurious noise caused by the unwanted wave. However, as shown in FIGS. 5 to 9 , when the wave length of the IDT electrode is about 1.00λ₀, no spurious noise is generated, but in the cases where the wave length is about 0.90λ₀, about 0.95λ₀, about 1.05λ₀, and about 1.10λ₀, a large spurious noise is generated. On the other hand, at this time, since A₁ is about 0.0196, B₁ is about 0.0311, C₁ is about 29.58, A₂ is about 0.0562, B₂ is about 0.0456 and C₂ is about 32.53, a relationship of T×r<B₂ is established, such that the condition of B₂<T×r≤0.10λ₀ described above is not satisfied. Therefore, in the case of the comparative example, a large spurious noise is generated in some cases within the range of the desired wave length of the IDT electrode, and when the electrode finger pitches of the IDT electrodes are different and the wave lengths are different on the same piezoelectric substrate, it is difficult to reduce or prevent the unwanted wave.

FIG. 10 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment is set to about 1.00λ₀. FIG. 11 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment is set to about 0.90λ₀. FIG. 12 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment is set to about 0.95λ₀. FIG. 13 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment is set to about 1.05λ₀. FIG. 14 is a graph showing return loss when the wave length of the IDT electrode of the acoustic wave resonator of the first preferred embodiment is set to about 1.10λ₀.

As shown in FIGS. 10 to 14 , in the first preferred embodiment, even when the wave length of the IDT electrode is varied in a range from about 0.90λ₀ to about 1.10λ₀, it is understood that the unwanted wave is effectively reduced or prevented.

Here, in the same manner as described above, when X is about 0.10, λ₁ is about 1.10λ₀ and λ₂ is about 0.90λ₀, and the return loss characteristics of the first acoustic wave resonator correspond to FIG. 14 and the return loss characteristics of the second acoustic wave resonator correspond to FIG. 11 . As shown in FIGS. 10 to 14 , it is understood that spurious noise due to the unwanted wave is effectively reduced or prevented in a case where any value in the range from about 0.90λ₀ to about 1.10λ₀ is the wave length of the IDT electrode. On the other hand, the values of A₁, B₁, C₁, A₂, B₂, and C₂ at this time are the same or substantially the same as those in the comparative example. In this case, with respect to the film thickness T of the main electrode layer of the IDT electrode in the first preferred embodiment, Expression 1 represents the relationship of about 29.09≤θ≤ about 31.27, so that θ in the first preferred embodiment satisfies Expression 1. Therefore, even when the electrode finger pitches of the IDT electrodes are different and the wavelengths are different on the same piezoelectric substrate, it is possible to effectively reduce or prevent the unwanted wave.

Hereinafter, the above Expressions 1 through 8 will be described in detail. For this purpose, while using FIGS. 15 to 20 described below, the reference of a fractional bandwidth of the unwanted wave able to sufficiently reduce or prevent the unwanted wave will be provided first. Next, examples in which the value of X is varied will be provided to indicate that the unwanted wave can be sufficiently reduced or prevented by satisfying the above Expressions 1 through 8.

FIGS. 15 to 19 described below show the results of return loss measurement obtained by varying θ in the acoustic wave resonator under the same conditions as those in the acoustic wave resonator of the first preferred embodiment used in the return loss measurement shown in FIG. 10 . The wave length of the IDT electrode was set to about 1.00λ₀, and θ in Euler angles (φ, θ, ψ) was varied in a range from above 28° to about 32°. As described above, in the Euler angles (φ, θ, ψ), φ was set to about 0° and ψ was also set to about 0°.

FIG. 15 is a graph showing return loss of the acoustic wave resonator in which the wave length of the IDT electrode is 1.00λ₀, in the case where θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 28°. FIG. 16 is a graph showing return loss of the acoustic wave resonator in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 29°. FIG. 17 is a graph showing return loss of the acoustic wave resonator in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 30°. FIG. 18 is a graph showing return loss of the acoustic wave resonator in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 31°. FIG. 19 is a graph showing return loss of the acoustic wave resonator in which the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 32°.

As shown in FIG. 15 , when θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 28°, it is understood that spurious noise caused by the unwanted wave is not sufficiently reduced or prevented. In general, in return loss of an acoustic wave resonator, when the absolute value of spurious noise caused by an unwanted wave is larger than about 0.3 dB, there arises a problem that characteristics of the acoustic wave device are significantly deteriorated.

For example, when a ladder acoustic wave filter is defined by using an acoustic wave resonator in which spurious noise is generated, it is known that spurious noise having a size of about one-half to about two-thirds of the size of the spurious noise observed in the return loss of the acoustic wave resonator is generated within the pass band of the acoustic wave filter. Accordingly, when the magnitude of the absolute value of the spurious noise caused by the unwanted wave is about 0.3 dB in the return loss of the acoustic wave resonator, spurious noise having a size of about 0.15 dB to about 0.2 dB is generated within the pass band of the acoustic wave filter.

Note that FIG. 30 shows a transmission characteristic of an acoustic wave filter when spurious noise having a size of about 0.2 dB is generated within the pass band of the acoustic wave filter. The horizontal axis in FIG. 30 represents a normalized frequency in which the frequency generating the spurious noise is 1. Generally speaking, the spurious noise of the size shown in FIG. 30 is considered not to raise a problem. Therefore, when the magnitude of the absolute value of spurious noise caused by the unwanted wave is about 0.3 dB in the return loss of the acoustic wave resonator, a situation in which the spurious noise affects operations of the acoustic wave filter, a high frequency front end circuit, and a communication apparatus using the stated acoustic wave resonator is considerably reduced or prevented.

On the other hand, when the magnitude of the absolute value of the spurious noise caused by the unwanted wave is about 0.4 dB in the return loss of the acoustic wave resonator, spurious noise having a size of about 0.2 to about 0.27 dB is generated within the pass band of the acoustic wave filter. FIG. 31 shows a transmission characteristic of the acoustic wave filter when spurious noise having a size of about 0.27 dB is generated within the pass band of the acoustic wave filter. The horizontal axis in FIG. 31 represents a normalized frequency in which the frequency at which the spurious noise is generated is 1. The spurious noise of the size shown in FIG. 31 may raise a problem in the acoustic wave filter. Therefore, when the magnitude of the absolute value of spurious noise caused by the unwanted wave is about 0.4 dB in the return loss of the acoustic wave resonator, it is understood that the spurious noise may affect the operations of the acoustic wave filter, the high frequency front end circuit, and the communication apparatus using the acoustic wave resonator.

As discussed above, when the magnitude of the absolute value of the spurious noise caused by the unwanted wave is greater than about 0.3 dB in the return loss of the acoustic wave resonator, the spurious noise may affect the operations of the acoustic wave filter, high frequency front end circuit, and communication apparatus using the stated acoustic wave resonator. Therefore, by reducing the magnitude of the absolute value of the spurious noise to equal to or smaller than about 0.3 dB in the return loss characteristics of the acoustic wave resonator, it is possible to reduce or prevent the deterioration in filter characteristic of the acoustic wave filter, the high frequency front end circuit, and the communication apparatus using the acoustic wave resonator.

As shown in FIGS. 16 to 18 , when the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is set to equal to or greater than about 29° and equal to or smaller than about 31°, the magnitude of the absolute value of the spurious noise is able to be set to equal to or smaller than about 0.3 dB. On the other hand, as shown in FIG. 19 , in the case where θ is about 32°, the spurious noise caused by the unwanted wave is unable to be sufficiently reduced or prevented.

FIG. 20 is a graph showing a relationship between θ in Euler angles (φ, θ, ψ) of a piezoelectric substrate and a fractional bandwidth of an unwanted wave, in an acoustic wave resonator in which a wave length of an IDT electrode is about 1.00λ₀. Note that the unwanted wave in FIG. 20 is an SH wave. Since the size of the fractional bandwidth of the unwanted wave and the size of the spurious noise correspond to each other, the smaller the size of the fractional bandwidth is, the more it is possible to reduce or prevent the spurious noise. The conditions of the acoustic wave resonator used for the measurement in FIG. 20 are the same or substantially the same as those of the acoustic wave resonator of the first preferred embodiment used for the return loss measurement shown in FIG. 10 , except that θ is varied. The same applies to the acoustic wave resonators in FIGS. 21, 23, 25, and 27 to be described later.

As shown in FIG. 20 , when the wave length of the IDT electrode is about 1.00λ₀, in the case where θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 30°, the fractional bandwidth of the unwanted wave is nearly 0%. As θ takes a value separate from about 30°, the fractional bandwidth of the unwanted wave becomes larger. In the above, it is indicated that, with reference to FIG. 16 , when θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate is about 29°, the magnitude of the absolute value of the spurious noise caused by the unwanted wave can be set to equal to or smaller than about 0.3 dB so that it is possible to sufficiently reduce or prevent the spurious noise. As shown in FIG. 20 , when θ is about 29°, it is understood that the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%. Therefore, the spurious noise caused by the unwanted wave can be sufficiently reduced or prevented in the range of θ in which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%.

Under the conditions of the first preferred embodiment shown in FIG. 20 , the range of θ in which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005% is represented by the relationship of about 28.9°≤θ≤ about 31.4°. Therefore, when the wave length of the IDT electrode is about 1.00λ₀ and is a single one, by selecting the above range of θ, the spurious noise caused by the unwanted wave can be sufficiently reduced or prevented.

Next, examples in which the value of X is varied will be described below.

In the acoustic wave device 1 of the first preferred embodiment, among the plurality of IDT electrodes, the wave length λ₁ of the first IDT electrode is the longest and the wavelength λ₂ of the second IDT electrode is the shortest. As described above, the wavelength λ₁ and the wavelength λ₂ can be represented, using the average value λ₀ of the wave length λ₁ and wave length λ2, by an expression of λ₁=(1+X)λ₀ and an expression of μ₂=(1−X)λ₀. Hereinafter, in the acoustic wave device 1, a range of θ able to sufficiently reduce or prevent spurious noise caused by the unwanted wave is determined in a case where the wave length takes any value equal to or greater than λ₂ and equal to or smaller than λ₁ among the plurality of IDT electrodes.

Here, when X is set to about 0.05, the above-mentioned range of θ at which the fractional bandwidth of the unwanted wave becomes equal to or smaller than about 0.005% in the first IDT electrode and the second IDT electrode, is shown in FIG. 21 described below.

FIG. 21 is a graph showing a relationship among the wave length of the IDT electrode in the acoustic wave resonator, θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate, and the fractional bandwidth of the unwanted wave, in the case where X is about 0.05. A solid line indicates a result of the case where the wave length of the IDT electrode is λ₀. A broken line indicates a result corresponding to the first IDT electrode having a wave length of about 1.05λ₀. A dot-dash line indicates a result corresponding to the second IDT electrode having a wave length of about 0.95λ₀. The result indicated by the solid line is the same or substantially the same as the result shown in FIG. 20 .

As shown in FIG. 21 , it is understood that the range of θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005% differs depending on the wave length of the IDT electrode. When the wave length of the IDT electrode falls within a range from about 0.95λ₀ to about 1.05λ₀, the fractional bandwidth of the unwanted wave can be made equal to or smaller than about 0.005% in the range of about 29.01°≤θ≤ about 31.29° indicated by an arrow D1 in FIG. 21 . The line representing the relationship between θ and the fractional bandwidth when the wave length of the IDT electrode falls within the range from about 0.95λ₀ to about 1.05λ₀ is present in a region between the broken line and the dot-dash line in FIG. 21 . Accordingly, by selecting θ in the range indicated by the arrow D1, the unwanted wave can be sufficiently reduced or prevented in a case where the wave length of the IDT electrode takes any value in the range from about 0.95λ₀ to about 1.05λ₀.

When the film thickness of the main electrode layer of the IDT electrode is different, the relationship between θ in the Euler angles (φ, θ, ψ) and the fractional bandwidth of the unwanted wave is changed. The same or substantially the same evaluation as that in FIG. 21 was performed while varying the thickness of the main electrode layer to obtain a relationship between the film thickness of the main electrode layer and upper and lower limit values of θ at which the fractional bandwidth of the unwanted wave was equal to or smaller than about 0.005%. The results thereof are shown in Table 1 below and FIG. 22 .

TABLE 1 Pt film Lower limit Upper limit thickness value value (λ) of θ (°) of θ (°) 0.050 25.64 25.98 0.055 27.29 28.41 0.060 27.93 29.54 0.065 28.32 30.20 0.070 28.60 30.63 0.075 28.78 30.92 0.080 28.92 31.13 0.085 29.01 31.29 0.090 29.09 31.42 0.095 29.15 31.52 0.100 29.19 31.60 0.105 29.22 31.67 0.110 29.24 31.73 0.115 29.25 31.78 0.120 29.27 31.82

FIG. 22 is a graph showing a relationship between the film thickness of the main electrode layer and the upper and lower limit values of θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate at which the fractional bandwidth of the unwanted wave in the acoustic wave resonator is equal to or smaller than about 0.005%, in the case where X is about 0.05. A curved line E1 indicated by a solid line in FIG. 22 shows a relationship between the film thickness of the main electrode layer and the lower limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%. A curved line F1 indicated by a broken line shows a relationship between the film thickness of the main electrode layer and the upper limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%.

The curved line E1 in FIG. 22 is represented by an equation of θ=−0.028/(T_(Pt)−0.043)+29.70 when the film thickness of the main electrode layer is T_(Pt). The curved line F1 is represented by an equation of θ=−0.060/(T_(Pt)−0.041)+32.62. A region surrounded by the curved line E1 and the curved line F1 in FIG. 22 is a region where the unwanted wave can be sufficiently suppressed. This region can be represented by Expression 9 given below. −0.028/(T _(Pt)−0.043)+29.70≤θ≤−0.060/(T _(Pt)−0.041)+32.62  Expression 9

As described above, the main electrode layer of the IDT electrode in the first preferred embodiment is preferably made of Pt, for example. T_(Pt) in Expression 9 is a value obtained by normalizing, with λ₀, the film thickness when the main electrode layer is made of Pt. The lower limit value of the film thickness T_(Pt) in the case of X being about 0.05 is a film thickness at the intersection point of the curved line E1 and the curved line F1, and is about 0.049λ₀.

On the other hand, when the film thickness of the main electrode layer becomes too large, the aspect ratio of the IDT electrode becomes excessively large, thus making it difficult to form the IDT electrode. Further, when the aspect ratio of the IDT electrode is large, the aspect ratio of a gap between the IDT electrodes is also large, so that voids or cracks are likely to be generated in the first dielectric film in this portion. Therefore, it is preferable for the film thickness T_(Pt) when the main electrode layer is made of Pt to be equal to or smaller than about 0.12λ₀, and is more preferable to be equal to or smaller than about 0.10λ₀, for example. In this specification, the aspect ratio of the IDT electrode is a ratio of the film thickness of the electrode finger of the IDT electrode to the dimension along a transverse direction of the electrode finger. The aspect ratio of the gap between the IDT electrodes is a ratio of the film thickness of the electrode fingers adjacent to each other across the gap, to the dimension along the transverse direction of the gap.

When a metal other than Pt is used for the main electrode layer, the film thickness of the main electrode layer may be set to a film thickness corresponding to a density ratio of the above metal and Pt. More specifically, when the density of Pt is ρ_(Pt), and the density of the metal used for the main electrode layer is ρ, the density ratio is represented by ρ/ρ_(Pt). When the film thickness of the main electrode layer is T, and the density ratio is represented by an equation of r=ρ/ρ_(Pt), the relationship between the film thickness T and the film thickness T_(Pt) in the above Expression 9 is represented by an equation of T_(Pt)=T/(ρ_(Pt)/ρ)=T×r. By substituting this into Expression 9, Expression 10 can be achieved as follows. −0.028/(T×r−0.043)+29.70≤θ≤−0.060/(T×r−0.041)+32.62  Expression 10

It is preferable that T×r in Expression 10 fall within a range of about 0.049λ₀≤T×r≤ about 0.10λ₀.

Expression 10 indicates a range of θ able to effectively suppress the unwanted wave in the case of X being about 0.05. Expression 10 is an expression achieved by assigning respective numerical values to A₁, B₁, C₁, A₂, B₂, and C₂ in Expression 1 described below. −A ₁/(T×r−B ₁)+C ₁ ≤θ≤−A ₂/(T×r−B ₂)+C ₂  Expression 1

Also in a case where X takes a value other than about 0.05, it is possible to indicate the range of θ able to effectively reduce or prevent the unwanted wave by an expression achieved by assigning respective numerical values to A₁, B₁, C₁, A₂, B₂, and C₂ in Expression 1. Hereinafter, examples in which X takes values other than about 0.05 will be given to indicate that it is possible to suppress the unwanted wave by satisfying the above expressions 1 through 8 even when X is varied.

FIG. 23 is a graph showing a relationship among the wave length of the IDT electrode in the acoustic wave resonator, θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate, and the fractional bandwidth of the unwanted wave, in the case where X is about 0.10. A solid line indicates a result of the case where the wave length of the IDT electrode is λ₀. A broken line indicates a result of the case where the wave length is about 1.10λ₀. A dot-dash line indicates a result of the case where the wave length is about 0.90λ₀.

As shown in FIG. 23 , when the wave length of the IDT electrode falls within a range from equal to or greater than about 0.90λ₀ to equal to or smaller than about 1.10λ₀, the fractional bandwidth of the unwanted wave can be made equal to or smaller than about 0.005% in the range of about 29.11°≤θ≤ about 31.13° indicated by an arrow D2. The line representing the relationship between θ and the fractional bandwidth when the wave length of the IDT electrode falls within the range from about 0.90λ₀ to about 1.10λ₀ is present in a region between the broken line and the dot-dash line in FIG. 23 . Accordingly, the unwanted wave can be sufficiently reduced or prevented by selecting θ in the range indicated by the arrow D2 in a case where the wave length of the IDT electrode takes any value in the range from about 0.90λ₀ to about 1.10λ₀.

In addition, the same evaluation as that in FIG. 23 was performed while varying the thickness of the main electrode layer to obtain a relationship between the film thickness of the main electrode layer and upper and lower limit values of θ in the Euler angles (φ, θ, ψ) at which the fractional bandwidth of the unwanted wave was equal to or smaller than about 0.005%. The results thereof are shown in Table 2 below and FIG. 24 .

TABLE 2 Pt film Lower limit Upper limit thickness value value (λ) of θ (°) of θ (°) 0.060 28.30 28.80 0.065 28.59 29.72 0.070 28.79 30.28 0.075 28.93 30.66 0.080 29.03 30.93 0.085 29.11 31.13 0.090 29.16 31.28 0.095 29.21 31.40 0.100 29.23 31.51 0.105 29.25 31.58 0.110 29.26 31.65 0.115 29.27 31.71 0.120 29.28 31.76

FIG. 24 is a graph showing a relationship between the film thickness of the main electrode layer and the upper and lower limit values of θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate at which the fractional bandwidth of the unwanted wave in the acoustic wave resonator is equal to or smaller than 0.005%, in the case where X is about 0.10. A curved line E2 indicated by a solid line in FIG. 24 shows a relationship between the film thickness of the main electrode layer and the lower limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%. A curved line F2 indicated by a broken line shows a relationship between the film thickness of the main electrode layer and the upper limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%.

A region surrounded by the curved line E2 and the curved line F2 in FIG. 24 is a region where the unwanted wave can be sufficiently reduced or prevented, in the case where X is about 0.10. By making T_(Pt) to be T×r, this region can be represented by Expression 11 given below. The lower limit value of T×r in the case of X being about 0.10 is seen at the intersection point of the curved line E2 and the curved line F2, and is about 0.058λ₀. −0.020/(T×r−0.044)+29.61≤θ≤−0.057/(T×r−0.045)+32.53  Expression 11

It is preferable that T×r in Expression 11 fall within a range of about 0.058λ₀≤T×r≤about 0.10λ₀, for example.

FIG. 25 is a graph showing a relationship among the wave length of the IDT electrode in the acoustic wave resonator, θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate, and the fractional bandwidth of the unwanted wave, in the case where X is about 0.15. A solid line indicates a result of the case where the wave length of the IDT electrode is λ₀. A broken line indicates a result of the case where the wave length is about 1.15λ₀. A dot-dash line indicates a result of the case where the wave length is about 0.85λ₀.

As shown in FIG. 25 , when the wave length of the IDT electrode falls within a range from about 0.85λ₀ to about 1.15λ₀, the fractional bandwidth of the unwanted wave can be made equal to or smaller than about 0.005% in the range of about 29.18λ₀ about 30.94° indicated by an arrow D3. The line representing the relationship between θ and the fractional bandwidth when the wave length of the IDT electrode falls within the range from about 0.85λ₀ to about 1.15λ₀ is present in a region between the broken line and the dot-dash line in FIG. 25 . Accordingly, the unwanted wave can be sufficiently reduced or prevented by selecting θ in the range indicated by the arrow D3 in a case where the wave length of the IDT electrode takes any value in the range from about 0.85λ₀ to about 1.15λ₀.

In addition, the same evaluation as that in FIG. 25 was carried out while varying the thickness of the main electrode layer to obtain a relationship between the film thickness of the main electrode layer and upper and lower limit values of θ in the Euler angles (φ, θ, ψ) at which the fractional bandwidth of the unwanted wave was equal to or smaller than about 0.005%. The results thereof are shown in Table 3 below and FIG. 26 .

TABLE 3 Pt film Lower limit Upper limit thickness value value (λ) of θ (°) of θ (°) 0.065 28.81 29.10 0.070 28.95 29.86 0.075 29.06 30.35 0.080 29.13 30.70 0.085 29.18 30.94 0.090 29.22 31.13 0.095 29.24 31.28 0.100 29.26 31.39 0.105 29.27 31.50 0.110 29.28 31.57 0.115 29.28 31.63 0.120 29.28 31.69

FIG. 26 is a graph showing a relationship between the film thickness of the main electrode layer and the upper and lower limit values of θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate at which the fractional bandwidth of the unwanted wave in the acoustic wave resonator is equal to or smaller than about 0.005%, in the case where X is about 0.15. A curved line E3 indicated by a solid line in FIG. 26 shows a relationship between the film thickness of the main electrode layer and the lower limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%. A curved line F3 indicated by a broken line shows a relationship between the film thickness of the main electrode layer and the upper limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%.

A region surrounded by the curved line E3 and the curved line F3 in FIG. 26 is a region where the unwanted wave can be sufficiently reduced or prevented, in the case where X is about 0.15. By making T_(Pt) to be T×r, this region can be represented by Expression 12 below. The lower limit value of T×r in the case of X being about 0.15 is seen at the intersection point of the curved line E3 and the curved line F3, and is about 0.064λ₀. −0.012/(T×r−0.047)+29.50≤θ≤−0.055/(T×r−0.049)+32.48  Expression 12

It is preferable that T×r in Expression 12 fall within a range of about 0.064λ₀≤T×r≤ about 0.10λ₀, for example.

FIG. 27 is a graph showing a relationship among the wave length of the IDT electrode in the acoustic wave resonator, θ in Euler angles (φ, θ, ψ) of the piezoelectric substrate, and the fractional bandwidth of the unwanted wave, in the case where X is about 0.20. A solid line indicates a result of the case where the wave length of the IDT electrode is λ₀. A broken line indicates a result of the case where the wave length is about 1.20λ₀. A dot-dash line indicates a result of the case where the wave length is about 0.80λ₀.

As shown in FIG. 27 , when the wave length of the IDT electrode falls within a range from about 0.80λ₀ to about 1.20λ₀, the fractional bandwidth of the unwanted wave can be made equal to or smaller than about 0.005% in the range of about 29.24°≤θ≤ about 30.73° indicated by an arrow D4. The line representing the relationship between θ and the fractional bandwidth when the wave length of the IDT electrode falls within the range from about 0.80λ₀ to about 1.20λ₀ is present in a region between the broken line and the dot-dash line in FIG. 27 . Accordingly, the unwanted wave can be sufficiently reduced or prevented by selecting θ in the range indicated by the arrow D4 in a case where the wave length of the IDT electrode takes any value in the range from about 0.80λ₀ to about 1.20λ₀.

In addition, the same or substantially the same evaluation as that in FIG. 27 was carried out while varying the thickness of the main electrode layer to obtain a relationship between the film thickness of the main electrode layer and upper and lower limit values of θ in the Euler angles (φ, θ, ψ) at which the fractional bandwidth of the unwanted wave was equal to or smaller than about 0.005%. The results thereof are shown in Table 4 below and FIG. 28 .

TABLE 4 Pt film Lower limit Upper limit thickness value value (λ) of θ (°) of θ (°) 0.070 29.09 29.33 0.075 29.16 29.99 0.080 29.21 30.42 0.085 29.24 30.73 0.090 29.26 30.96 0.095 29.28 31.13 0.100 29.29 31.28 0.105 29.29 31.39 0.110 29.29 31.48 0.115 29.28 31.56 0.120 29.27 31.62

FIG. 28 is a graph showing a relationship between the film thickness of the main electrode layer and the upper and lower limit values of θ in the Euler angles (φ, θ, ψ) of the piezoelectric substrate at which the fractional bandwidth of the unwanted wave in the acoustic wave resonator is equal to or smaller than about 0.005%, in the case where X is about 0.20. A curved line E4 indicated by a solid line in FIG. 28 shows a relationship between the film thickness of the main electrode layer and the lower limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%. A curved line F4 indicated by a broken line shows a relationship between the film thickness of the main electrode layer and the upper limit value of θ at which the fractional bandwidth of the unwanted wave is equal to or smaller than about 0.005%.

A region surrounded by the curved line E4 and the curved line F4 in FIG. 28 is a region where the unwanted wave can be sufficiently reduced or prevented, in the case where X is about 0.20. By making T_(Pt) to be T×r, this region can be represented by Expression 13 below. The lower limit value of T×r in the case of X being about 0.20 is seen at the intersection point of the curved line E4 and the curved line F4, and is about 0.069λ₀. −0.008/(T×r−0.048)+29.45≤θ≤−0.050/(T×r−0.054)+32.36  Expression 13

It is preferable that T×r in Expression 13 fall within a range of about 0.069λ₀≤T×r≤about 0.10λ₀, for example.

In the above, when X was about 0.05, about 0.10, about 0.15, and about 0.20, the above-mentioned range of θ able to effectively reduce or prevent the unwanted wave was determined. Similarly, also when X was equal to or greater than about 0.25 and equal to or smaller than about 0.65, the range of θ able to effectively reduce or prevent the unwanted wave was determined. The range of each θ when X was varied was determined as an expression in which respective numerical values were assigned to A₁, B₁, C₁, A₂, B₂, and C₂ in Expression 1 described below. The values of A₁, B₁, C₁, A₂, B₂, and C₂ are shown in Table 5 below.

TABLE 5 X A₁ B₁ C₁ A₂ B₂ C₂ 0.05 0.0328 0.0417 29.76 0.0596 0.0412 32.62 0.10 0.0203 0.0444 29.59 0.0566 0.0453 32.53 0.15 0.0125 0.0461 29.49 0.0532 0.0496 32.46 0.20 0.0068 0.0485 29.42 0.0504 0.0541 32.37 0.25 0.0038 0.0498 29.39 0.0476 0.0589 32.31 0.30 0.0025 0.0507 29.39 0.0455 0.0632 32.26 0.35 0.0020 0.0510 29.38 0.0443 0.0663 32.19 0.40 0.0020 0.0510 29.38 0.0432 0.0695 32.13 0.45 0.0020 0.0510 29.38 0.0430 0.0721 32.06 0.50 0.0020 0.0510 29.38 0.0433 0.0743 32.03 0.55 0.0020 0.0510 29.38 0.0438 0.0766 31.98 0.60 0.0020 0.0510 29.38 0.0453 0.0782 31.94 0.65 0.0020 0.0510 29.38 0.0467 0.0804 31.90

Based on these results, A₁, B₁, C₁, A₂, B₂, and C₂ were determined as Expressions 2 through 8 described below using X. −A ₁/(T×r−B ₁)+C ₁ ≤θ≤−A ₂/(T×r−B ₂)+C ₂  Expression 1

A₁, B₁, C₁, A₂, B₂, and C₂ in Expression 1 are represented by Expressions 2 through 8 given below using X. A ₁=0.056×10^(−4.93×x)+0.0016  Expression 2 B ₁=−0.088×X ²+0.066×X+0.0386(0.05≤X≤0.375)  Expression 3 B ₁=0.051(0.375≤X≤0.65)  Expression 4 C ₁=0.714×10^(−5.26×x)+28.37  Expression 5 A ₂=0.0987×X ²−0.0918×X+0.0644  Expression 6 B ₂=−0.0651×X ²+0.1114×X+0.0351  Expression 7 C ₂=0.7830×X ²−1.7424×X+32.70  Expression 8

As discussed above, by satisfying Expressions 1 through 8, it is possible to effectively reduce or prevent the unwanted wave even when the IDT electrodes having different electrode finger pitches are provided on the same piezoelectric substrate.

When T×r equals B₁ in the left side of Expression 1, the denominator becomes 0 so that θ diverges. Similarly, when T×r equals B₂ in the right side of Expression 1, the denominator becomes 0 so that θ diverges. Further, as described above, it is preferable for the film thickness of the main electrode layer of the IDT electrode to be equal to or smaller than about 0.12λ₀, and is more preferable to be equal to or smaller than about 0.10λ₀, for example. Therefore, in the present preferred embodiment, the relationship of B₁<T×r≤0.10λ₀, and the relationship of B₂<T×r≤0.10λ₀ are determined. When the film thickness of the main electrode layer is equal to or smaller than about 0.10λ₀, in the case where X exceeds about 0.65, the above θ does not have a range in which it is possible to sufficiently reduce or prevent the unwanted wave. Accordingly, in the first preferred embodiment, X is preferably set to be equal to or smaller than about 0.65, for example.

In the acoustic wave device 1, as illustrated in FIG. 2 , the film thickness of the first IDT electrode 4A and the film thickness of the second IDT electrode 4B are equal or substantially equal. The film thickness of a portion of the first dielectric film 8 provided on the first IDT electrode 4A and the film thickness of a portion thereof provided on the second IDT electrode 4B are also equal or substantially equal. Accordingly, the first band pass filter and the second band pass filter in the acoustic wave device 1 can be formed at the same time. As described above, in the first preferred embodiment, unwanted waves can be effectively reduced or prevented without complicating the process.

The acoustic wave device 1 of the first preferred embodiment is a composite filter device used for carrier aggregation or the like. In the following, it will be described that the acoustic wave device 1 is able to effectively reduce or prevent unwanted waves in combinations of various communication bands. Table 6 below shows examples of combinations of communication bands used in carrier aggregation and a center frequency ratio of a reception band of each communication band.

TABLE 6 Communication Center band combination frequency ratio Band38-Band7  1.023 Band25-Band4  1.087  Band4-Band30 1.104  Band7-Band40 1.130 Band1-Band3 1.161  Band8-Band20 1.169  Band3-Band66 1.170  Band5-Band13 1.174  Band5-Band12 1.195 Band25-Band30 1.200 Band66-Band41 1.203  Band1-Band41 1.212 Band66-Band7  1.232 Band1-Band7 1.241 Band4-Band7 1.245  Band3-Band40 1.275 Band25-Band41 1.321 Band39-Band41 1.365  Band1-Band21 1.423 Band66-Band21 1.433  Band1-Band11 1.440 Band3-Band7 1.441 Band66-Band11 1.450

In order to make the pass band of a band pass filter be a desired band, it is necessary to set the wave length determined by the electrode finger pitch of the IDT electrode in the acoustic wave resonator to a wave length corresponding to the desired band. As the center frequency ratio of the combined communication bands is larger, a difference in electrode finger pitch between the IDT electrodes in the acoustic wave resonators becomes larger between one band pass filter and the other band pass filter.

As described before, the first band pass filter 3A illustrated in FIG. 1 is provided with the first acoustic wave resonator including the first IDT electrode having the longest wave length of λ₁. Accordingly, the wave length of the IDT electrode of the acoustic wave resonator in the acoustic wave device 1 is equal to or smaller than λ₁. On the other hand, the second band pass filter 3B is provided with the second acoustic wave resonator including the second IDT electrode having the shortest wave length of λ₂. Accordingly, the wave length of the IDT electrode of the acoustic wave resonator in the acoustic wave device 1 is equal to or greater than λ₂.

The maximum wave length ratio between the acoustic wave resonator of the first band pass filter 3A and the acoustic wave resonator of the second band pass filter 3B can be represented by an equation of λ₁/λ₂=(1+X)λ₀/(1−X)λ₀=(1+X)/(1−X). Accordingly, the wave length ratio between the acoustic wave resonator forming the pass band of the first band pass filter 3A and the acoustic wave resonator forming the pass band of the second band pass filter 3B is equal to or smaller than (1+X)/(1−X). When the center frequency ratio between the communication band to which the first band pass filter 3A belongs and the communication band to which the second band pass filter 3B belongs is equal to or smaller than (1+X)/(1−X), the configuration of the first preferred embodiment may be achieved. In this case, unwanted waves can be effectively reduced or prevented.

Here, in the first preferred embodiment, the relationship of about 0.05≤X≤ about 0.65 is satisfied. For example, when X is about 0.05, a relationship of λ₁/λ₂=(1+X)/(1−X)=about 1.105 is established. On the other hand, the center frequency ratio between Band4 and Band30 shown in Table 6 is about 1.104. Therefore, when the communication bands of a center frequency ratio equal to or smaller than the center frequency ration between Band4 and Band30 are combined, it is possible to effectively reduce or prevent unwanted waves.

In addition, for example, when X is about 0.20, λ₁/λ₂ equals about 1.50. Therefore, when the communication bands of a center frequency ratio equal to or smaller than the center frequency ration between Band66 and Band11 shown in Table 6 are combined, it is possible to effectively reduce or prevent unwanted waves. As described thus far, unwanted waves can be effectively reduced or prevented in the combinations of various communication bands.

The acoustic wave device 1 of the first preferred embodiment is preferably a composite filter. The acoustic wave device of the present invention is not limited to the above-described acoustic wave device, and may be, for example, an acoustic wave device including a plurality of acoustic wave filters provided on the same piezoelectric substrate and not connected commonly. A plurality of connected commonly acoustic wave filters and a plurality of not connected commonly acoustic wave filters may be mixed. Alternatively, the acoustic wave device of the present invention may be a ladder filter. As in these cases, even in a case where a plurality of IDT electrodes having different electrode finger pitches is provided on the same piezoelectric substrate, unwanted waves can be effectively reduced or prevented.

The above-described acoustic wave device may be used as a duplexer or the like of a high frequency front end circuit. An example thereof will be described below.

FIG. 29 is a configuration diagram of a communication apparatus and a high frequency front end circuit. In FIG. 29 , elements connected to a high frequency front end circuit 230, such as an antenna device 202 and an RF signal processing circuit (RFIC) 203, for example, are also illustrated. The high frequency front end circuit 230 and the RF signal processing circuit 203 define a communication apparatus 240. The communication apparatus 240 may include a power supply, a CPU, a display, and the like, for example.

The high frequency front end circuit 230 includes a switch 225, duplexers 201A and 201B, filters 231 and 232, low-noise amplifier circuits 214 and 224, and power amplifier circuits 234 a, 234 b, 244 a, and 244 b. Note that the high frequency front end circuit 230 and the communication apparatus 240 illustrated in FIG. 29 are an example of the high frequency front end circuit and the communication apparatus, and are not limited to this configuration.

The duplexer 201A includes filters 211 and 212. The duplexer 201B includes filters 221 and 222. The duplexers 201A and 201B are connected to the antenna device 202 via the switch 225. The above-described acoustic wave device may be used for the duplexers 201A and 201B, or may be used for the filters 211, 212, 221, and 222.

Further, the above-described acoustic wave device may be applied to, for example, a multiplexer including three or more filters, such as a triplexer in which an antenna terminal for three filters is shared and a hexaplexer in which an antenna terminal for six filters is shared.

That is, the acoustic wave device includes an acoustic wave resonator, a filter, a duplexer, and a multiplexer having three or more filters. The multiplexer is not limited to a configuration including both of a transmission filter and a reception filter, and may be configured to include only a transmission filter or a reception filter.

The switch 225 connects the antenna device 202 to a signal path corresponding to a predetermined band in accordance with a control signal from a control unit (not illustrated), and is preferably defined by, for example, a single pole double throw (SPDT) type switch. Note that the number of signal paths connected to the antenna device 202 is not limited to one, and there may be a plurality of signal paths. In other words, the high frequency front end circuit 230 may support carrier aggregation.

The low-noise amplifier circuit 214 is a reception amplifier circuit configured to amplify a high frequency signal (a high frequency reception signal in this case) coming through the antenna device 202, the switch 225 and the duplexer 201A, and output the amplified high frequency signal to the RF signal processing circuit 203. The low-noise amplifier circuit 224 is a reception amplifier circuit configured to amplify a high frequency signal (a high frequency reception signal in this case) coming through the antenna device 202, the switch 225 and the duplexer 201B, and output the amplified high frequency signal to the RF signal processing circuit 203.

The power amplifier circuits 234 a and 234 b are transmission amplifier circuits configured to amplify a high frequency signal (a high frequency transmission signals in this case) output from the RF signal processing circuit 203, and output the amplified high frequency signal to the antenna device 202 via the duplexer 201A and the switch 225. The power amplifier circuits 244 a and 244 b are transmission amplifier circuits configured to amplify a high frequency signal (a high frequency transmission signals in this case) output from the RF signal processing circuit 203, and output the amplified high frequency signal to the antenna device 202 via the duplexer 201B and the switch 225.

The RF signal processing circuit 203 performs signal processing, by down-conversion or the like, on a high frequency reception signal input from the antenna device 202 through a reception signal path, and outputs a reception signal having been generated by the signal processing. The RF signal processing circuit 203 performs signal processing, by up-conversion or the like, on an input transmission signal, and outputs a high frequency transmission signal having been generated by the signal processing to the power amplifier circuits 234 a, 234 b, 244 a, and 244 b. The RF signal processing circuit 203 is preferably, for example, an RFIC. The communication apparatus may include a baseband (BB) IC. In this case, the BBIC performs signal processing on the reception signal having been processed by the RFIC. Further, the BBIC performs signal processing on a transmission signal and outputs the signal to the RFIC. The reception signal having been processed by the BBIC, the transmission signal before the signal processing by the BBIC, and the like are, for example, an image signal and a sound signal.

According to the high frequency front end circuit 230 and the communication apparatus 240 configured as described above, unwanted waves can be effectively reduced or prevented.

The high frequency front end circuit 230 may include duplexers according to a modification of the duplexers 201A and 201B in place of the duplexers 201A and 201B.

On the other hand, the filters 231 and 232 in the communication apparatus 240 are connected between the RF signal processing circuit 203 and the switch 225 without passing through the low-noise amplifier circuits 214, 224 and the power amplifier circuits 234 a, 234 b, 244 a, and 244 b. The filters 231 and 232 are also connected to the antenna device 202 via the switch 225, similarly to the duplexers 201A and 201B.

Thus far, the acoustic wave devices, the high frequency front end circuits, and the communication apparatuses according to the preferred embodiments of the present invention have been described while referring to the preferred embodiments and the modifications thereof. However, other preferred embodiments achieved by combining arbitrary elements of the above preferred embodiments and modifications, modifications obtained by making variations conceived by those skilled in the art on the preferred embodiments described above without departing from the spirit and scope of the present invention, various equipment incorporating the high frequency front end circuit and the communication apparatus according to the present invention, and the like are also included in the present invention.

Preferred embodiments of the present invention may be widely used in communication equipment such as mobile phones, for example, as an acoustic wave resonator, a filter, a duplexer, a multiplexer applicable to a multi-band system, a front end circuit, and a communication apparatus.

While preferred embodiments of the present invention have been described above, it is to be understood that variations and modifications will be apparent to those skilled in the art without departing from the scope and spirit of the present invention. The scope of the present invention, therefore, is to be determined solely by the following claims. 

What is claimed is:
 1. An acoustic wave device comprising: a piezoelectric substrate made of LiNbO₃; a plurality of interdigital transducer (IDT) electrodes provided on the piezoelectric substrate and including a first IDT electrode and a second IDT electrode; and a dielectric film on the piezoelectric substrate and covering the plurality of IDT electrodes; wherein the first IDT electrode and the second IDT electrode include main electrode layers made of a material including W; among the plurality of IDT electrodes, a wave length λ1 determined by an electrode finger pitch of the first IDT electrode is the longest and a wave length λ2 determined by an electrode finger pitch of the second IDT electrode is the shortest; an average value λ₀ of the wave length λ₁ and the wave length λ₂ is defined by equations of λ₀=(λ₁+λ₂)/2, λ₁/λ₀=1+X, and λ₂/λ₀=1−X; X is not smaller than 0.05 and not larger than 0.65; and in Euler angles (φ, θ, ψ) of the piezoelectric substrate, φ is 0°±5° and ψ is 0°±10°.
 2. The acoustic wave device according to claim 1 wherein the first IDT electrode and the second IDT electrode further include conductive auxiliary electrode layers above the main electrode layers; the main electrode layer of the first IDT electrode has a largest mass among metal layers in the first IDT electrode; and the main electrode layer of the second IDT electrode has a largest mass among metal layers in the second IDT electrode.
 3. The acoustic wave device according to claim 2, wherein the conductive auxiliary electrode layers are made of a material including Al.
 4. The acoustic wave device according to claim 3, wherein the dielectric film includes a first dielectric layer made of SiO₂ and a second dielectric layer made of SiN on the first dielectric layer; and the second dielectric layer is thinner than the first dielectric layer.
 5. The acoustic wave device according to claim 4, wherein the first IDT electrode includes a contact layer between the main electrode layer and the piezoelectric substrate; and the second IDT electrode includes a contact layer between the main electrode layer and the piezoelectric substrate.
 6. The acoustic wave device according to claim 5, wherein the second dielectric layer is thinner than the main electrode layers.
 7. The acoustic wave device according to claim 6, wherein a thickness of the first IDT electrode is substantially the same as a thickness of the second IDT electrode.
 8. The acoustic wave device according to claim 7, wherein the second dielectric layer is thinner than the conductive auxiliary electrode layers.
 9. An acoustic wave device comprising: a piezoelectric substrate made of LiNbO₃; a plurality of interdigital transducer (IDT) electrodes provided on the piezoelectric substrate and including a first IDT electrode and a second IDT electrode; and a dielectric film on the piezoelectric substrate and covering the plurality of IDT electrodes; wherein the first IDT electrode and the second IDT electrode include main electrode layers made of a material including W; among the plurality of IDT electrodes, a wave length λ1 determined by an electrode finger pitch of the first IDT electrode is the longest and a wave length λ2 determined by an electrode finger pitch of the second IDT electrode is the shortest; an average value λ₀ of the wave length λ₁ and the wave length λ₂ is defined by an equation of λ₀=(λ₁+λ₂)/2; thicknesses of the main electrodes are not smaller than 0.049λ₀/(ρ/ρ_(Pt)) and not larger than 0.10λ₀/(ρ/ρ_(Pt)), ρ being a density of the material of the main electrode layers and ρ_(Pt) being a density of Pt; and in Euler angles (φ, θ, ψ) of the piezoelectric substrate, φ is 0°±5° and ψ is 0°±10°.
 10. The acoustic wave device according to claim 9, wherein: the first IDT electrode and the second IDT electrode further include conductive auxiliary electrode layers above the main electrode layers; the main electrode layer of the first IDT electrode has a largest mass among metal layers in the first IDT electrode; and the main electrode layer of the second IDT electrode has a largest mass among metal layers in the second IDT electrode.
 11. The acoustic wave device according to claim 10, wherein the conductive auxiliary electrode layers are made of a material including Al.
 12. The acoustic wave device according to claim 11, wherein: the dielectric film includes a first dielectric layer made of SiO₂ and a second dielectric layer made of SiN on the first dielectric layer; and the second dielectric layer is thinner than the first dielectric layer.
 13. The acoustic wave device according to claim 12, wherein: the first IDT electrode includes a contact layer between the main electrode layer and the piezoelectric substrate; and the second IDT electrode includes a contact layer between the main electrode layer and the piezoelectric substrate.
 14. The acoustic wave device according to claim 13, wherein the second dielectric layer is thinner than the main electrode layers.
 15. The acoustic wave device according to claim 14, wherein a thickness of the first IDT electrode is substantially the same as a thickness of the second IDT electrode.
 16. The acoustic wave device according to claim 15, wherein the second dielectric layer is thinner than the conductive auxiliary electrode layers.
 17. An acoustic wave device comprising: a piezoelectric substrate made of LiNbO₃; a plurality of interdigital transducer (IDT) electrodes provided on the piezoelectric substrate and including a first IDT electrode and a second IDT electrode; and a dielectric film on the piezoelectric substrate and covering the plurality of IDT electrodes; wherein the first IDT electrode and the second IDT electrode include main electrode layers made of a material including W; among the plurality of IDT electrodes, a wave length λ1 determined by an electrode finger pitch of the first IDT electrode is the longest and a wave length λ2 determined by an electrode finger pitch of the second IDT electrode is the shortest; an average value λ₀ of the wave length λ₁ and the wave length λ₂ is defined by an equation of λ₀=(λ₁+λ₂)/2; thicknesses of the main electrodes are not smaller than 0.049λ₀/(ρ/ρ_(Pt)) and not larger than 0.10 λ0/(ρ/ρ_(Pt)), ρ being a density of the material of the main electrode layers and ρ_(Pt) being a density of Pt; and the acoustic wave device uses a Rayleigh wave.
 18. The acoustic wave device according to claim 17, wherein: the average value λ₀ of the wave length λ₁ and the wave length λ₂ is further defined by equations of λ₁/λ₀=1+X, and λ₂/λ₀=1−X; and X is not smaller than 0.05 and not larger than 0.65.
 19. The acoustic wave device according to claim 18, wherein: the first IDT electrode and the second IDT electrode further include conductive auxiliary electrode layers above the main electrode layers; the main electrode layer of the first IDT electrode has a largest mass among metal layers in the first IDT electrode; and the main electrode layer of the second IDT electrode has a largest mass among metal layers in the second IDT electrode.
 20. The acoustic wave device according to claim 19, wherein the conductive auxiliary electrode layers are made of a material including Al.
 21. The acoustic wave device according to claim 20, wherein the dielectric film includes a first dielectric layer made of SiO₂ and a second dielectric layer made of SiN on the first dielectric layer; and the second dielectric layer is thinner than the first dielectric layer.
 22. The acoustic wave device according to claim 21, wherein: the first IDT electrode includes a contact layer between the main electrode layer and the piezoelectric substrate; and the second IDT electrode includes a contact layer between the main electrode layer and the piezoelectric substrate.
 23. The acoustic wave device according to claim 22, wherein the second dielectric layer is thinner than the main electrode layers.
 24. The acoustic wave device according to claim 23, wherein a thickness of the first IDT electrode is substantially the same as a thickness of the second IDT electrode.
 25. The acoustic wave device according to claim 24, wherein the second dielectric layer is thinner than the conductive auxiliary electrode layers. 